Different Molarity of Alkaline Activator

Divakar M

Abstract


A soluble base arrangement, a watery arrangement of sodium hydroxide, and sodium silicate, are utilized to alkalize silicon-and aluminum-rich materials to create geopolymer concrete. Salt response transformed into different in unique molar consideration as eight M, 10 M, 12 M, and 14 M with hydroxide to silicate proportion of 2.5. Two unique arrangement of substantial examples have been casted which were viz. Fly debris essentially based handiest use in the geopolymer concrete. Every one of the examples had been restored at 60 °C in broiler and raised relieving tank for 24 hours and climatic restoring in lab till 7 days and 28th day. It was discovered that oven-drying had a slightly better strength than steam-curing, and it became popular.


Full Text:

PDF

References


R. Anuradha, V. Sreevidya, R. Venkatasubraminan. Modified guidelines for geopolymer concrete mix design using Indian Standard method. October 2006.

M. Pratap Kishanrao. Design of Geopolymer Concrete. International Journal of Innovative Research in Science, Engineering and Technology, 2011.2(5).

M.S. Shetty. Concrete Technology – Theory and Practice. S. Chand and Company LTD, new corrected edition 2005.

IS 9013:1978, Method of making, curing and determining compressive strength of accelerated cured concrete test specimens. Bureau of Indian Standards, New Delhi.

IS 12119:1978, General requirements


Refbacks

  • There are currently no refbacks.